What are the differences between iron vanadium nitride and vanadium nitrogen alloy?
Mechanical property fluctuation value: The σs fluctuation value of the vanadium nitride-added iron steel is on average 45Mpa smaller than that of the vanadium-nitrogen alloy, the σb fluctuation value is on average 28Mpa smaller than the vanadium-nitrogen alloy, and the δ5 fluctuation value is 1% smaller than the vanadium-nitrogen alloy on average ( stable ingredients)
Vanadium absorption rate: Ferrovanadium nitride is 3 to 5 percentage points higher than vanadium-nitrogen alloy. (specific gravity)
Strengthening effect: Iron vanadium nitride is higher than vanadium nitrogen alloy. (high nitrogen to vanadium ratio)
Strengthening effect: Iron vanadium nitride is higher than vanadium nitrogen alloy. (high nitrogen to vanadium ratio)
Comprehensive comparison, the average vanadium saving is more than 10% (the use value of each unit of vanadium is increased)