Ferrosilicon Standard Block Processing And Customization
Ferrosilicon Standard Block Processing And Customization
Ferrosilicon Standard Block Processing And Customization

Ferrosilicon 65 Standard Block

The Ferrosilicon 65 Standard Block production process is based on the reduction of silica. 65 Fe Silicon Lumps are used as deoxidizing and alloying additives for the smelting of electrical, spring, corrosion, and heat-resistant steels.

Send Inquiry

Ferrosilicon_65_Technical_Product_Document.pdf

Product Introduction

Products Description

Ferrosilicon 65 Standard Block is widely used in the steelmaking industry to improve the quality of steel products. It is a combination of iron, silicon, and other elements, which can greatly enhance the physical and chemical properties of steel. With the increasing demand for steel products, the ferrosilicon block processing industry has been developing rapidly. The following article will introduce the processing and customization of ferrosilicon standard blocks.

65 Fe Silicon Lumps manufacturer

Firstly, the raw materials for ferrosilicon blocks are carefully selected. The quality of raw materials directly affects the performance of the final product. Therefore, strict quality control is necessary for the production of ferrosilicon blocks. The raw materials are usually purchased from reliable suppliers and tested for their chemical composition and physical properties before use. The quality of the raw materials is also checked during the production process to ensure that the final product meets the quality standards.

Secondly, the processing of ferrosilicon blocks involves the melting of raw materials. The melting process is carried out in a furnace at a high temperature. The raw materials are added to the furnace and heated until they melt and become homogeneous. During the melting process, any impurities are removed, and the chemical composition of the ferrosilicon block is adjusted to meet the desired specifications.

Thirdly, the melted ferrosilicon is poured into a mold and allowed to cool and solidify. The ferrosilicon block is then removed from the mold and inspected for defects. Any defects found are corrected, and the ferrosilicon block is polished to achieve a smooth surface. The final product is then packaged and prepared for shipment.

65 Fe Silicon Lumps manufacturer 65 Fe Silicon Lumps supplier

Products Content

Ferro silicon code	Chemical composition(%)
	Si	Mn	Cr	C	P	S
FeSi75A	74.0-80.0	≤0.4	≤0.3	≤0.1	≤0.035	≤0.02
FeSi75B	72.0-80.0	≤0.4	≤0.3	≤0.1	≤0.04	≤0.02
FeSi75C	70.0-80.0	≤0.5	≤0.5	≤0.2	≤0.04	≤0.02
FeSi65	65.0-72.0	≤0.6	≤0.5	≤0.2	≤0.04	≤0.02